Why would I want to cryogenically treat tool steels? Does it really affect the microstructure?

Minfa Lin
Senior Principal Research Engineer, Ph.D.

After austenitizing and quenching, tool steels are sometimes subjected to cold treatment at approximately –80°C, followed by tempering. Primarily, the cold treatment is done to increase strength, improve dimensional or microstructure stability, and improve wear resistance. These benefits are due to the transformation of retained austenite to martensite. Some studies show that lowering the cold treatment temperature below
–100°C does not significantly increase the amount of retained austenite-to-martensite transformation—therefore it does not result in additional benefits. However, other studies show that compared to cold treatment (–80°C), cryogenic treatment (–190°C) further improves wear resistance. For help determining which subzero quenching process can help you produce the best parts, call us at 800-654-4567.

← Back to Quenching
An error has occured, please fix the highlighted fields.
To request a quote or for more information about Air Products, please fill out the form below, and an Air Products representative will contact you shortly.
Please use the form below to contact us.

What can we answer for you?

  1. What kind of inquiry?

If you would prefer to contact us by phone, you can call any of our Air Products locations worldwide by visiting Worldwide Locations & Phone Numbers.


This site uses cookies to store information on your computer. Some are essential to make our site work; others help us to better understand our users. By using the site, you consent to the placement of these cookies. Read our Legal Notice to learn more.